Обший каталог Yamawa 2016 - 2017 - страница 826

Предыдущая страница Следующая страница

Навигация

Surface Treatment

M3×0.52.642.62
M4×0.73.543.52
M5×0.84.404.38
M6×15.305.28
M8×1.257.107.07
M1×0.250.8080.785M2.3×0.41.9981.968
M1.1×0.250.9180.891M2.3×0.252.0962.071
M1.2×0.251.0070.984M2.5×0.452.1622.126
M1.4×0.31.1681.142M2.5×0.352.2282.196
M1.6×0.351.3321.300M2.6×0.452.2622.226
M1.7×0.351.4321.401M2.6×0.352.3182.278
M1.8×0.351.5301.498M3×0.52.6272.589
M2×0.41.6991.669M3×0.352.7182.677
M2×0.251.7961.771M4×0.53.6073.561
M2.2×0.451.8631.827M5×0.54.6064.560
S0.5×0.1250.4100.396
S0.6×0.150.4940.479
S0.7×0.1750.5750.559
S0.8×0.20.6580.640
S0.9×0.2250.7410.720

The best surface treatment is applied to each tap depending on the tapping purpose. Characteristics and effectiveness of surface treatment are introduced at next section.

■Oxidizing

This treatment was processed by using HOMO furnace being made by LEED AND NORTHUP company USA in 1938, and it is called HOMO treatment. This treatment is also called vapor treatment and steam treatment. Through this treatment, Fe O layer of blue black color is produced over the tool 3 4 surface. Oxidization treatment produces porous layer on tool's surface. This porous layer works as oil pocket to reduce friction, to avoid welding and to improve the surface roughness of internal screw. Moreover, longer tool life is expected because the treatment reduces the remaining stress of HSS tools. This treatment does not increase the hardness on tool surface. Using the furnace of YAMAWA original design and choosing the proper treatment time, we have marked good result of oxidizing for YAMAWA HSS tools. Stainless steel and low carbon steel are the materials that are easy to get welding. We are applying this treatment to the special purpose taps for these materials to get good result. Further due to the reduction of friction force, this treatment has good result for wide range of steel type material. We combine oxidizing with nitriding for the taps designed for thermal refined steels of high carbon steels and alloy steels. This double treatment wins good reputation of the market.

■Thickness of oxide layer and the time of treatment ■Comparison between bright and oxide treated

Cutting condition

Tap : SU-SP/M8×1.25/P2 Material : X5 CrNi 18 9 (165~171HB) Hole size : 6.8mm Tapping Length : 12mm (through hole) Tapping Speed : 7.2m/min Cutting oil : Insoluble oil Tapping Machine : CNC tapping machine

SU-SP design SU-SP

(minute) (Bright) (Oxide treated)

Treatment time

TechnicalTechnical-51-000