| For | Turning (CV | D) | | | | | |
| Work Material | Grade H | ardness (HRA) | TRS (GPa) | Coating Type C | oating Thickness (μ | m) Features | Old Grades |
| AC810P | 91.0 | 2.2 | Super FF Coat | 18 | · For high-speed and high-efficiency machining of steel ·Grade emphasising wear resistance for high- to medium-speed cutting | AC700G |
| AC8015P | 91.0 | 2.3 | Absotech | 14 | · For high-speed and high-efficiency machining of steel · Crystal orientation control technology is used to drastically suppress the advancement of crater wear, achieving long, stable tool life during high-speed and high feed cutting | AC810P |
| AC820P | 90.1 | 2.2 | Super FF Coat | 14 | · General-purpose grade with a superior balance of fracture and wear resistance | AC2000 |
| Steel | AC8025P | 90.1 | 2.3 | Absotech | 12 | · Our 1st recommended grade for turning steel · Smooth surface treatment suppresses abnormal damage from adhesion/chipping while realizing stable tool life over a wide range of work materials and cutting speeds | AC820P |
| AC830P | 89.4 | 2.6 | Super FF Coat | 8 | · For interrupted machining of steel · Tough grade with an emphasis on fracture resistance | AC3000 |
| AC8035P | 89.4 | 2.6 | Absotech | 9 | · For interrupted machining of steel ·Coating layertensile stress removal technology greatly improves fracture resistance and achieves long, stable tool life during heavy interrupted cutting | AC830P |
| AC610M | 91.0 | 2.2 | Super FF Coat | 5 | · For high-speed machining of stainless steel · Grade emphasising wear resistance for high-efficiency machining | — |
| AC6020M | 90.1 | 2.3 | Absotech | 5 | · For high-speed machining of stainless steel · Adopts a high-hardness carbide substrate and new coating to realise excellent wear resistance and fracture resistance, resulting in stable long tool life in high-speed machining | AC610M |
| Stainless Steel | AC6030M | 89.5 | 2.7 | Absotech | 5 | · Our 1st recommended grade for turning stainless steel · Drastically reduces the occurrence of abnormal damage in stainless steel machining and achieves long and stable tool life thanks to the new coating | AC630M |
| AC630M | 89.5 | 2.7 | Super FF Coat | 5 | · General-purpose grade with a superior balance of fracture and wear resistance for stainless steel machining ·Supports continuous and light cutting of steel with low cutting speeds | AC304 |
| AC405K | 92.0 | 2.4 | Super FF Coat | 18 | · For high-speed cast iron milling ·Grade emphasising wear resistance for high- to medium-speed cutting | AC410K |
| AC4010K | 91.1 | 2.5 | Absotech | 20 | · Our 1st recommended grade for turning gray cast iron · For high-speed cast iron milling · New thick coating realises stable long tool life even with ultra- high-speed machining of gray cast iron atVC= 700 m/min | AC405K |
| Cast Iron | AC4015K | 91.1 | 2.5 | Absotech | 16 | · Our 1st recommended grade for turning ductile cast iron ·New high-adhesion, high-strength coating realises high wear resistance and chipping resistance for stable long tool life over a wide range of cutting conditions | AC415K |
| AC415K | 91.1 | 2.5 | Super FF Coat | 18 | · General-purpose grade with a superior balance of fracture and wear resistance | AC410K |
| AC420K | 91.1 | 2.5 | Super FF Coat | 12 | · For interrupted machining of cast iron ·Designed as a grade with emphasis on fracture resistance and chipping resistance, outstanding stability is realised with heavy interrupted cutting | AC700G |
| | | | | | and unstable cutting of cast iron | |
| For | Milling (CVD | ) | | | | | |
| Work Material | Grade H | ardness (HRA) | TRS (GPa) | Coating Type C | oating Thickness (μ | m) Features | Old Grades |
| ACP100 | 89.3 | 3.1 | Super FF Coat | 6 | · For high-speed machining of steel · Grade emphasising wear resistance for high-speed machining | AC230 |
| Steel | ACP2000 | 89.5 | 3.2 | Absotech | 10 | · For high-speed machining of steel · Stable long tool life with high-speed machining is realised by adopting a tough carbide substrate and a new coating with excellent thermal crack resistance | ACP100 |
| Stainless Steel | ACM200 | 89.8 | 3.4 | Super FF Coat | 6 | · For machining high-hardness stainless steel · Adopts newly developed high-strength cemented carbide with excellent wear resistance and thermal resistance, realizing outstanding stability when machining hardened stainless steel | AC230 |
| ACK100 | 92.0 | 2.4 | Super FF Coat | 6 | · For high-speed cast iron milling · Adopts a high-hardness substrate as a grade with high wear resistance | — |
| Cast Iron | ACK200 | 91.7 | 2.5 | Super FF Coat | 6 | · For high-speed cast iron milling · Adopts a tough carbide substrate as a grade with excellent wear resistance and thermal crack resistance | AC211 |
| ACK2000 | 91.7 | 3.1 | Absotech | 10 | · For high-speed cast iron milling · Stable long tool life with high-speed machining is realised by adopting a tough carbide substrate and a new coating with excellent thermal resistance | ACK100 ACK200 |
Каталог Sumitomo запасные части
Каталог Sumitomo сплавы и режимы
Техническая информация Sumitomo
Каталог Sumitomo пластины с алмазными вставками Sumidia
Каталог Sumitomo специальные торцевые фрезы
Общий каталог Sumitomo 2018 - 2019