Общий каталог Lamina Technologies 2019 - 2020 - страница 138
Навигация
Общий каталог Lamina Technologies 2017 - 2018
MACHINING CONDITIONS | MILLING - LT 30 - LT 3000 MACHINING CONDITIONS | MILLING - LT 3000
APKT 1705 PETR XPKW 0602-HF
| Material | Lamina | Material | Hardness | D [m | OC m] | Fe [m | ed m/z] | V [m/ | c min] | Sugg P | ested St aramete | arting rs |
| Group | Gr. N° | Examples | min | max | min | max | min | max | DOC | Feed | Vc | |
| C35, Ck45, | 125 HB | 330 | 250 | |||||||||
| Non Alloyed | 1 | 1020, 1045, | 190 HB | 0.50 | 15.00 | 0.18 | 0.40 | 190 | 300 | 4.00 | 0.28 | 220 |
| 1060, 28Mn6 | 250 HB | 250 | 200 | |||||||||
| 42CrMo4 | 180 HB | 031 | 150 | 240 | 024 | 200 | ||||||
| Low Alloyed | 2 | , St50, Ck60, | 230 HB | 050 | 1500 | 015 | . | 210 | 400 | . | 180 | |
| P | 4140, 4340, | 280 HB | . | . | . | 190 | . | 150 | ||||
| 100Cr6 | 350 HB | 0.27 | 130 | 170 | 0.22 | 140 | ||||||
| 220 HB | 027 | 90 | 150 | 022 | 130 | |||||||
| X40CrMoV5, | 280 HB | . | 130 | . | 120 | |||||||
| High Alloyed | 3 | H13, M42, D3, | 0.50 | 10.70 | 0.12 | 3.00 | ||||||
| S6-5-2 12Ni19 | 320 HB | 110 | 100 | |||||||||
| , | 350 HB | 0.22 | 60 | 90 | 0.19 | 80 | ||||||
| Atiti | 4 | 304, 316, | 180 HB | 050 | 1500 | 0.15 | 0.31 | 190 | 250 | 400 | 024 | 220 |
| usenc | X5CrNi18-9 | 240 HB | . | . | 0.12 | 0.27 | 160 | 210 | . | . | 190 | |
| M Duplex | 5 | X2CrNiN23-4, S31500 | 290 HB 310 HB | 0.50 | 10.70 | 0.12 | 0.22 | 70 | 130 120 | 3.00 | 0.19 | 100 90 |
| Ferritic & | 410, X6Cr17, | 200 HB | 15.00 | 0.31 | 150 | 210 | 4.00 | 0.24 | 190 | |||
| Martensitic | 6 | 17-4PH, 430 | 42 HRc | 0.50 | 10.70 | 0.15 | 0.25 | 90 | 150 | 3.00 | 0.19 | 130 |
| GG20 GG40 EN- | 150 HB | 240 | 200 | |||||||||
| Grey | 7 | , , GJL-250, | 200 HB | 0.50 | 15.00 | 0.18 | 0.40 | 150 | 220 | 4.00 | 0.28 | 180 |
| N030B | 250 HB | 190 | 160 | |||||||||
| K | GGG40 | 150 HB | 200 | 180 | ||||||||
| Malleable & Nodular | 8 | , GGG70, | 200 HB | 0.50 | 15.00 | 0.15 | 0.35 | 100 | 180 | 4.00 | 0.24 | 150 |
| 50005 | 250 HB | 150 | 130 | |||||||||
| Incoloy 800 | 240 HB | 45 | 32 | |||||||||
| Fe, Ni & Co based | 9 | Inconel 700 | 250 HB | 0.50 | 10.70 | 0.12 | 0.22 | 25 | 45 | 3.00 | 0.19 | 30 |
| S | Stellite 21 | 350 HB | 45 | 30 | ||||||||
| TiAl6V4 | - | 0.25 | 30 | 55 | 0.22 | 40 | ||||||
| Ti based | 10 | T40 | - | 0.50 | 10.70 | 0.12 | 0.22 | 40 | 65 | 3.00 | 0.19 | 55 |
| X100 CrMo13 | 45 HRc | 5.40 | 0.22 | 80 | 2.00 | 0.17 | 60 | |||||
| Steel | , 440C, | 50 HRc | 3.20 | 0.20 | 70 | 1.50 | 0.16 | 55 | ||||
| H | 11 | G-X260NiCr42 | 55 HRc | 0.50 | 1.60 | 0.10 | 0.17 | 40 | 60 | 1.00 | 0.14 | 50 |
| Chilled Cast Iron | Ni-Hard 2 | 400 HB | 4.30 | 0.22 | 80 | 1.50 | 0.17 | 50 | ||||
| White Cast Iron | G-X300CrMo15 | 55 HRc | 1.60 | 0.17 | 30 | 60 | 1.00 | 0.14 | 40 | |||
| NF Aluminium | 12 | AlSi12 | 130 HB | 0.50 | 15.00 | 0.18 | 0.40 | 200 | 400 | 4.00 | 0.30 | 280 |
| Material Group | Lamina Gr. N° | Material Examples | Hardness | D [m | OC m] | Fe [m | ed m/z] | V [m/ | c min] | Sugg P | ested St aramete | arting rs |
| min | max | min | max | min | max | DOC | Feed | Vc | ||||
| C35, Ck45, | 125 HB | 330 | 250 | |||||||||
| Non Alloyed | 1 | 1020, 1045, | 190 HB | 0.20 | 0.50 | 0.20 | 1.40 | 190 | 300 | 0.50 | 1.00 | 220 |
| 1060, 28Mn6 | 250 HB | 250 | 200 | |||||||||
| 42CrMo4, | 180 HB | 150 | 240 | 040 | 080 | 200 | ||||||
| St50, Ck60, | 230 HB | 210 | . | . | 180 | |||||||
| P Low Alloyed | 2 | 4140, 4340, | 280 HB | 0.20 | 0.50 | 0.20 | 1.30 | 190 | 150 | |||
| 100Cr6 | 350 HB | 130 | 170 | 0.40 | 0.70 | 140 | ||||||
| 220 HB | 90 | 150 | 040 | 070 | 130 | |||||||
| Hih Alloed | 3 | X40CrMoV5, H13 M42 D3 | 280 HB | 020 | 040 | 020 | 110 | 130 | . | . | 120 | |
| g y | , , , S6-5-2, 12Ni19 | 320 HB | . | . | . | . | 60 | 110 | 040 | 060 | 100 | |
| 350 HB | 90 | . | . | 80 | ||||||||
| Ferritic & | 6 | 410, X6Cr17, | 200 HB | 020 | 040 | 020 | 0.50 | 150 | 210 | 040 | 040 | 190 |
| Martensitic | 17-4PH, 430 | 42 HRc | . | . | . | 0.60 | 90 | 150 | . | . | 130 | |
| GG20, GG40, EN- | 150 HB | 240 | 200 | |||||||||
| Grey | 7 | GJL-250, | 200 HB | 0.20 | 0.50 | 0.20 | 1.40 | 150 | 220 | 0.50 | 1.00 | 180 |
| K | N030B | 250 HB | 190 | 160 | ||||||||
| GGG40, | 150 HB | 200 | 050 | 180 | ||||||||
| Malleable & Nodular | 8 | GGG70, | 200 HB | 0.20 | 0.50 | 0.20 | 1.20 | 100 | 180 | . | 0.90 | 150 |
| 50005 | 250 HB | 150 | 0.40 | 130 | ||||||||
| X100 CrMo13, | 45 HRc | 0.40 | 0.80 | 80 | 0.40 | 0.50 | 60 | |||||
| Steel | 440C, | 50 HRc | 0.20 | 0.20 | 0.70 | 70 | 0.40 | 55 | ||||
| H | 11 | G-X260NiCr42 | 55 HRc | 0.30 | 0.50 | 40 | 60 | 0.30 | 0.30 | 50 | ||
| Chilled Cast Iron | Ni-Hard 2 | 400 HB | 0.20 | 0.30 | 0.20 | 0.50 | 80 | 0.30 | 0.40 | 50 | ||
| White Cast Iron | G-X300CrMo15 | 55 HRc | 0.20 | 0.30 | 0.20 | 0.50 | 30 | 60 | 0.30 | 0.30 | 40 |