Общий каталог SGS 2021 - страница 341

METRIC Carbon Composite Ap Series Ae Ae DC • mm 20M Vc Metric Ae x DC Ap x DC (m/min) 3 6 8 10 12 Slot 1 ≤1 120(96-164) RPM 12722 6361 4771 3817 3181Fr0.0550.1130.2430.3660.439 Feed (mm/min) 700 720 1160 1395 1395 RPM 15903 7951 5963 4771 3976 CFRP, AFRP(CARBON FIBER,ARAMID FIBER)Profile≤ 0.5 ≤ 1.5 150(120-180) Fr 0.055Feed (mm/min)8750.113900 0.2431450 0.3661744 0.4391744 HSM ≤ 0.05 ≤2 250(200-300) RPMFr 26504 13252 9939 7951 66260.1260.2600.5560.8331.000 Feed (mm/min) 3350 3450 5527 6625 6625 Slot 1 ≤1 100(80-120) RPM 10602 5301 3976 3181 2650Fr0.0540.1110.2360.3570.428 Feed (mm/min) 570 587 940 1135 1135 GFRP(FIBERGLASS) Profile ≤ 0.5 ≤ 1.5 120(96-164) RPM 12722 6361 4771 3817 3181Fr0.0540.1110.2360.3570.428 Feed (mm/min) 684 704 1128 1362 1362 HSM ≤ 0.05 ≤2 200(160-240) RPMFr 21203 10602 7951 6361 53010.1240.2610.5571.0111.213 Feed (mm/min) 2629 2765 4430 6430 6430 N Slot 1 ≤1 145(116-174) RPMFr 15372 7686 5765 4612 38430.0690.1520.3230.4820.579 Feed (mm/min) 1061 1165 1860 2224 2224 ProfileCARBON, GRAPHITE≤ 0.5 ≤ 1.5 185(148-222) RPMFr 19613 9807 7355 5884 49030.0690.1520.3230.4820.579 Feed (mm/min) 1353 1486 2373 2838 2838 HSM ≤ 0.05 ≤2 300(240-360) RPMFr 31805 15903 11927 9542 79510.1590.3480.7401.1091.331 Feed (mm/min) 5057 5535 8820 10580 10580 Slot 1 ≤1 245(196-294) RPMFr 25974 12987 9740 7792 64940.0690.1500.3190.4770.572 Feed (mm/min) 1792 1945 3107 3717 3717 PLASTICS Profile ≤ 0.5 ≤ 1.5 305(244-366) RPMFr 32335 16168 12126 9701 80840.0690.1500.3190.4770.572 Feed (mm/min) 2231 2421 3868 4627 4627 HSM ≤ 0.05 ≤2 505(404-606) RPMFr 53538 26769 20077 16062 133850.1590.3440.7321.0971.316 Feed (mm/min) 8513 9220 14690 17617 17617 HSM (high speed machining) finish cuts typically required reduced feed and cutting depths rpm = (Vc x 1000) / (DC x 3.14) rates shown are for use without coolant; rates may be increased with coolant mm/min = Fr x rpm dust collection is vital when machining dry adjust parameters based on resin type and fiber structure diamond coating will increase tool life in graphite and composite materials reduce speed when overheating causes melting or damage to resin refer to the SGS Tool Wizard® for complete technical information reduce feed if delamination or fraying occur   (www.kyocera-sgstool.com) www.kyocerRaO-sUgTsEtRoSol.com ROUTERS 341